Traditional Chinese|
Product grade |
Type |
Softening point℃（a） |
Garner chroma(b) |
acid value（c） |
Abietic acid% |
Dehydroabietate |
Saponification value% |
Application |
|||||||||
|
TSR-675S |
Refined rosin |
≥75 |
≤3 |
≥170 |
≤0.5 |
≥70 |
≥160 |
Suitable for adhesive, hot melt adhesive, rubber used as emulsifier, synthetic rubber plasticizer and tackifier. Pigment surface treatment |
|||||||||
|
Product grade |
Melting point, C (capillary method) |
appearance |
Acid number (c) |
Abietic acid% |
Application |
||||||||||||
|
Abietic acid （DHA） |
≥150 |
White powder |
≥185 |
≥99.0 |
Physiological active substance, medicine Intermediates, pesticides, chemistryOptics Physiological active substance, medicine
|
||||||||||||
|
Product grade |
Type |
Softening point °c（a） |
chroma (b) |
acid value （c） |
Application |
||||||||||||
|
TSR-602 |
Modified rosin |
65-75 |
2MAX |
≤200 |
Solder paste, flux, adhesive, alcohol soluble ink Alcohol soluble film adhesive, can replace the water white hydrogenated rosin
|
||||||||||||
|
TSR-610 |
Modified rosin |
100-110 |
2MAX |
≥200 |
Solder paste, flux, adhesive, alcohol soluble ink Alcohol soluble adhesive at |
||||||||||||
|
TSR-685 |
Modified rosin |
120-130 |
2MAX |
≥230 |
Solder paste, flux, adhesive, alcohol soluble ink
|
||||||||||||
|
TSR-691 |
Modified rosin |
Viscous liquid |
8MAX |
180--200 |
Low temperature tin bismuth solder paste, good fluidity |
||||||||||||
|
Product grade |
Type |
Melting point, C (capillary method) |
Chroma (b) |
Acid number (C) |
Application |
||||||||||||
|
TSR-604 |
Special rosin |
130-140 |
White powder |
≤300 |
Lead free solder has a good supporting effect on the alloy |
||||||||||||
|
Product grade |
Type |
Melting point, C (capillary method) |
Chroma (b) |
（c）Acid number (c) |
Hydroxymethyl |
Application |
|||||||||||
|
TSR-526 |
Alkyl phenolic resin |
60-70 |
≤4 |
60-80 |
≥10 |
The use of chloroprene rubber, can improve the heat resistance and adhesion |
|||||||||||